MOULD SEALING ROPE is used for sealing the parting line of two moulding boxes. It is available in various sizes i.e. in diameters i.e. 4mm, 6mm, 9mm & 12mm.
MOULD SEALING ROPE is placed at the parting line of the drag half moulding box over the periphery and then cope half is placed over it.
Six months from the date of packing.
CHILLING COMPOUND is the best Chromite Sand media for chilling metal. It has the ability to draw heat from the molten metal allowing the metal to skin over faster and minimizing sand burn on. Thus will help to reduce casting rejections.
The Higher the Expansion, better the Slag Coagulation property. Expansion of SLAG COAGULANT is 18-24 CC.
Due to higher Expansion (18-24 cc),
Presence of extremely low or negligible fines helps to maintain clean atmosphere surrounding the furnace.
Storage in Cool & Dry place.
12 months from the date of manufacturing.
50 Kg. HDPE Bags.
When Slag Coagulant comes in contact with the metal, it reacts with the slag & starts coagulation i.e. formation of spongy agglomeration. The Coagulation depends on Expansion of Granules.
Cr2O3: 45-47%, SiO2: 1% Max., Fe2O3: 27-29%, Al2O3: 14.5%, CaO: 0.18 typical, Max 0.2%,
MgO: 10.2 Typical & max. 11%, TiO2: 0.69%, V2O5: 0.34%, P: 0.0029%, S: 0.0029%, Cr:Fe ratio: 1.58:1
Bulk density: 155-165 lbs/cu.ft
AFS No.: 40-50
SSK has entered into joint venture with M/s KAGALITE KOGYO CO. LTD. JAPAN .
This product was developed especially for Highest Safety to Furnace operator.
Extremely Low density 0.80 – 0.85 g/cc which is 50-60% of the ordinary perlite.
2) Expansion is 36cc against 23-24 cc of Ordinary perlite.
3) Addition rate is max 0.15% against 0.3-0.4% of perlite.
4) No spirting of metal results in high METAL cleanliness surrounding the furnace &
inside the plant.
5) Highest quality of Slag Coagulation & will help in minimizing rejection due to slag
inclusion at foundry as well as after machining stage.